How long to cure printed models?
Curing time depends on the type of resin. For modeling resins, we recommend curing for 10-30 minutes. It is enough that the surface does not stick and the model hardens. To achieve maximum toughness and hardness, the dental resins must be fully cured, a time of 30-60 minutes is recommended. Casting resins may not be cured for longer than 30 minutes.
How to wash printed models?
For dental and model resins, we recommend washing 2 x 3 minutes in an ultrasonic cleaner with IPA, but for casting resins 30-60 seconds in an IPA bath or just rinsing with IPA.
How to filter used material?
After printing, we always recommend filtering the resin using a 150-200 micron filter.
Material | Washing (IPA) | Casting | Curing |
Dental Sand A1 | 2 х 3min | 80°С @30min | 10min @405nm (200W) |
Dental Sand A2 | 2 х 3min | 80°С @30min | 30min @405nm (200W) |
Dental Sand A3 | 2 х 3min | 80°С @30min | 10min @405nm (200W) |
Dental Bleach | 2 х 3min | 80°С @60min | 5min @405nm (200W) |
Dental Yellow Clear | 2 х 3min | 70°С @10min | 15min @405nm (200W) |
Dental Yellow Clear (autokláv) | 2 х 3min | 60°С @10min | 1min @405nm (200W) |
Dental Clear | 2 х 3min | 70°С @10min | 10min @405nm (200W) |
Dental Peach | 2 х 3min | 70°С @10min | 15min @405nm (200W) |
Dental Pink | 2 х 3min | 70°С @10min | 30min @405nm (200W) |
Dental RO | 2 х 3min | 70°С @10min | 10min @405nm (200W) |
Dental Cast | 2 х 1min | 50°С @10min | 2min @405nm (200W) |
Model Natural Clear | 2 х 3min | 60°С @10min | 3min @405nm (200W) |
Model Clear | 2 х 3min | 60°С @10min | 3min @405nm (200W) |
Model Black | 2 х 3min | 60°С @10min | 15min @405nm (200W) |
Model Grey | 2 х 3min | 60°С @10min | 15min @405nm (200W) |
Model Cherry | 2 х 3min | 60°С @10min | 15min @405nm (200W) |
Model Blue | 2 х 3min | 60°С @10min | 15min @405nm (200W) |
Model White | 2 х 3min | 60°С @10min | 3min @405nm (200W) |
Basic Resin Red | 2 х 3min | 60°С @10min | 15min @405nm (200W) |
Industrial ABS | 2 х 3min | 60°С @10min | 15min @405nm (200W) |
Industial Flex | 2 х 3min | 60°С @10min | 15min @405nm (200W) |